Trung Quốc Nhà Máy Bán Buôn Giá Của Hạt Nhựa Chịu Nhiệt Độ Cao Nguyên Liệu ABS

5
68.700đ
24.500đ
64.3% giảm giá
Thông số sản phẩm
ABS
x8oIcnViL6
Mô tả sản phẩm
Nơi xuất xứ: TaiwanNhãn hiệu: Chi mei industrial

Số Mô Hình: PA-777ENơi Xuất Xứ: Đài Loan

Mô hình Số: PA-777EChất liệu: ABS

Sự xuất hiện: Sữa hạtĐóng gói: 25kg/bao

MFR: 4Mật độ: 1.07

Lớp: Đùn lớpMàu sắc: Màu trắng sữa

Cổng: Ningbo




Overview
Place of Origin
Taiwan
Brand Name
Chi mei industrial
AModel Number
PA-777E
Material
 ABS
Appearance
Milky grain
MFR
7.5
Grade
Extrusion grade
Density
1.03
CERTIFICATE
ISO SGS
MOQ
25 kg
Specification
Physical properties of
rating
Unit
The test method
 The density of
---3
1.07
g/cm³
ASTM D792
23℃
1.07
g/cm³
ISO 1183
Melt mass flow rate
4.0
g/10min
ASTM D1238
Volume flow rate of solution
4.50
cm³/10min
ISO 1133
shrinkage
0.30到0.60
%
ISO 294-4
Impact properties
rating
Unit
The test method
Notched impact strength of simply supported beam
ISO 179
-30℃
6.0
KJ/㎡
ISO 179
23℃
13
KJ/㎡
ISO 179
Notched impact strength of cantilever beam
23℃,3.2mm
120
J/m
ASTM D256
23℃,6.4mm
110
J/m
ASTM D256
-30℃
6.0
KJ/㎡
ISO 180-1A
23℃
12
KJ/㎡
ISO 180-1A
Thermal performance
rating
Unit
The test method
Thermal deformation temperature
1.8MPa,Without annealing
109
ASTM D648
1.8MPa,Without annealing
101
ISO 75-2/A
1.8MPa,annealing
120
ASTM D648
1.8MPa,annealing
121
ISO 75-2/A
VEKA softening temperature
A50
129
ISO 360/A50
B50
121
ISO 306
Linear coefficient of thermal expansion
MD
8.2E-5
1/℃
ISO 11359-2
Flame retardant performance
rating
Unit
The test method
Flame retardant grade
1.50mm
HB
UL 94
Mechanical properties of
rating
Unit
The test method
Rockwell hardness
Rated R
115
ASTM D785
The tensile strength
yield 4
44.0
MPa
ASTM D638
yield
45.0
MPa
ISO 527-2/50
The fracture
32.0
MPa
ISO 527-2/50
Tensile strain
The fracture 4
10
%
ASTM D638
The fracture
29
%
ISO 527-2/50
Bending modulus
--5
2210
MPa
ASTM D790
--6
2300
MPa
ISO 178
The bending strength
--5
68.3
MPa
ASTM D790
--6
74.0
MPa
ISO 178
Details Images
ABS profile
ABS plastic has the common performance of three kinds of components, A makes it resistant to chemical corrosion, heat resistance,
and has A certain surface hardness, B makes it has high elasticity and toughness, S makes it has the processing and forming
characteristics of thermoplastic plastic and improve the electrical performance. Therefore, ABS plastic is a kind of raw material
is easy to get, good comprehensive performance, cheap, widely used "tough, hard, rigid" material. ABS plastics have been widely
used in machinery, electrical, textile, automobile, aircraft, ship and other manufacturing industries and chemical industry.

General Performance of ABS

The appearance of ABS is opaque and ivory color granule, non-toxic, tasteless, low bibulous rate of its products can be into a
variety of colors, and has 90% high gloss. ABS has good combination with other materials and is easy to surface printing, coating
and coating treatment. ABS, a flammable polymer with an oxygen index of 18.2, has a yellow flame, black smoke, charred but not
dripping, and gives off a distinctive cinnamon smell.

Mechanical properties of ABS

ABS has excellent mechanical properties, its impact strength is good, can be used at very low temperature. Even if ABS products
are damaged, it can only be tensile damage but not impact damage. ABS has excellent wear resistance, good dimensional stability,
and oil resistance. It can be used for bearings under medium load and speed. The creep property of ABS is greater than that of PSF
and PC, but less than that of PA and POM. The bending strength and compression strength of ABS are poor among plastics. The
mechanical properties of ABS are greatly affected by temperature.

Thermal properties of ABS

ABS is an amorphous polymer with no obvious melting point. Melt viscosity is high, poor mobility, poor weather resistance,
ultraviolet light can make discoloration; The thermal deformation temperature is 70 -- 107℃ (about 85 ℃), and the product can be
increased by about 10℃ after annealing treatment. Sensitive to temperature and shear rate; ABS can still show certain toughness at
-40℃, and can be used for a long time in the temperature range from -40℃ to 85℃.
Product packaging
Quick Details:
Place of Origin:Taiwan
Model Number:PA-777E
Brand Name:Chi mei industrial


Supply Ability:
Supply Ability 50 Ton/Tons per Day


Packaging & Delivery:
Packaging Details 25kg/bag
Port SHANGHAI AND NINGBO
Picture Example:
Lead Time:
Quantity(kilograms)
1 - 100000
>100000
Est. Time(days)
7
To be negotiated